ixef? hc-1022 is a 50% glass-fiber reinforced, general purposepolyarylamide compound that exhibits very high strength andrigidity, outstanding surface gloss, and excellent creepresistance.ixef? hc-1022 shows no evidence of cytotoxicity,sensitization, intracutaneous reactivity or systemic toxicity basedon biocompatibility testing as defined by iso 10993:1. solvayoffers these materials for healthcare applications that re exposure (less than 24 hours) to the body

black: hc-1022 bk 000

natural: hc-1022 nt 000

gray: hc-1022 gy51

additional colors available

custom colorableixef? hc-1022 物性表

基本信息黄卡编号
填料/增强材料
特性
用途
机构评级
rohs 合规性
外观
形式
加工方法
物理性能干燥调节后的单位制测试方法密度1.64--g/cm3iso 1183收缩率0.10 到 0.30--%iso 294-4吸水率(23°c, 24 hr)0.16--%iso 62吸水性 - equil, 65% rh1.50--
内部方法机械性能干燥调节后的单位制测试方法拉伸模量1950019500mpaiso 527-2拉伸应力(断裂)280260mpaiso 527-2拉伸应变(断裂)1.92.2%iso 527-2弯曲模量18500--mpaiso 178弯曲应力380--mpaiso 178冲击性能干燥调节后的单位制测试方法悬壁梁缺口冲击强度110--j/mastm d256无缺口悬臂梁冲击850--j/mastm d256热性能干燥调节后的单位制测试方法热变形温度(1.8 mpa, 未退火)230--°ciso 75-2/a线形热膨胀系数 - 流动1.5e-5--cm/cm/°ciso 11359-2注射干燥单位制干燥温度120°c
干燥时间0.50 到 1.5hr
料筒后部温度250 到 260°c
料筒前部温度260 到 290°c
射嘴温度260 到 290°c
加工（熔体）温度280°c
模具温度120 到 140°c
注射速度快速

注射成型

粒子

黑色

灰色

可用颜色

自然色

rohs 合规

iso 10993

高光应用

外科器械

牙齿应用领域

医疗/护理用品

医疗器材

医疗器械

超强刚性

尺寸稳定性良好

出色的外观

低吸湿性

电子束消毒

放射性可透的

辐射消毒

高强度

好的消毒性

环氧乙烷消毒

抗伽马辐射

良好的抗蠕变性

流动性高

耐化学性良好

生物兼容性

通用

玻璃纤维增强材料, 50% 填料按重量