德国巴斯夫E2010G6聚醚砜树脂

basf ultrason e 2010 g6 30% glass filled pes 物性表

物理性能额定值 (公制)额定值 (英制)测试方法密度1.60 g/cc0.0578 lb/in³iso 1183吸水率1.6 %1.6%iso 62平衡吸湿0.60 %0.60 %23°c/50% r.h.; iso 62粘度测试56 cm³/g56cm³/gviscosity number线性成型收缩率,flow0.0028 cm/cm0.0028 in/iniso294线性成型收缩率，横向0.0058 cm/cm0.0058 in/iniso 294熔体流动速率25 g/10 min

@load 10.0 kg, temperature 360 °c

25 g/10 min

@load 22.0 lb, temperature 680 °f

iso 1133机械性能额定值 (公制)额定值 (英制)测试方法球压硬度224 mpa32500 psiiso2039-1抗张强度(断裂)140 mpa20300 psi5mm/min; iso 527-2
100 mpa

@temperature 140 °c

14500 psi

@temperature 284 °f

125 mpa

@temperature 100 °c

18100 psi

@temperature 212 °f

135 mpa

@temperature 60.0 °c

19600 psi

@temperature 140 °f

150 mpa

@temperature 20.0 °c

21800 psi

@temperature 68.0 °f

抗张强度31.0 mpa

@# of cycles 1.00e+7 , temperature 180 °c

4500 psi

@# of cycles 1.00e+7 , temperature 356 °f

38.0 mpa

@# of cycles 1.00e+6 , temperature 180 °c

5510 psi

@# of cycles 1.00e+6 , temperature 356 °f

43.0 mpa

@# of cycles 100000 , temperature 180 °c

6240 psi

@# of cycles 100000 , temperature 356 °f

50.0 mpa

@strain 0.600 %, temperature 160 °c

7250 psi

@strain 0.600 %, temperature 320 °f

iso 527
50.0 mpa

@strain 0.500 %, temperature 23.0 °c

7250 psi

@strain 0.500 %, temperature 73.4 °f

iso 527
75.0 mpa

@strain 1.00 %, temperature 160 °c

10900 psi

@strain 1.00 %, temperature 320 °f

iso 527
80.0 mpa

@strain 1.40 %, temperature 160 °c

11600 psi

@strain 1.40 %, temperature 320 °f

iso 527
80.0 mpa

@strain 1.00 %, temperature 23.0 °c

11600 psi

@strain 1.00 %, temperature 73.4 °f

iso 527
125 mpa

@strain 1.50 %, temperature 23.0 °c

18100 psi

@strain 1.50 %, temperature 73.4 °f

iso 527抗张强度(屈服)140 mpa20300 psi50mm/min; iso 527-2伸长率 (断裂)1.9 %1.9%5mm/min; iso 527-2屈服伸长率1.9 %1.9 %50mm/min; iso 527-2
0.189 %

@time 3600 sec, pressure 15.0 mpa

0.189 %

@time 1.00 hour, pressure 2180 psi

iso 899
0.19 %

@pressure 15.0 mpa, time 360000 sec

0.19 %

@pressure 2180 psi, time 100 hour

iso 899
0.20 %

@pressure 15.0 mpa, time 3.60e+7 sec

0.20 %

@pressure 2180 psi, time 10000 hour

iso 899
0.20 %

@pressure 10.0 mpa, time 360000 sec

0.20 %

@pressure 1450 psi, time 100 hour

180°c; iso 899
0.20 %

@time 3600 sec, pressure 10.0 mpa

0.20 %

@time 1.00 hour, pressure 1450 psi

180°c; iso 899
0.25 %

@pressure 10.0 mpa, time 3.60e+7 sec

0.25 %

@pressure 1450 psi, time 10000 hour

180°c; iso 899
0.30 %

@time 3600 sec, pressure 20.0 mpa

0.30 %

@time 1.00 hour, pressure 2900 psi

180°c; iso 899
0.30 %

@pressure 20.0 mpa, time 360000 sec

0.30 %

@pressure 2900 psi, time 100 hour

180°c; iso 899
0.30 %

@time 3600 sec, pressure 30.0 mpa

0.30 %

@time 1.00 hour, pressure 4350 psi

180°c; iso 899
0.35 %

@time 3600 sec, pressure 30.0 mpa

0.35 %

@time 1.00 hour, pressure 4350 psi

180°c; iso 899
0.38 %

@pressure 30.0 mpa, time 360000 sec

0.38 %

@pressure 4350 psi, time 100 hour

180°c; iso 899
0.40 %

@pressure 30.0 mpa, time 3.60e+7 sec

0.40 %

@pressure 4350 psi, time 10000 hour

iso 899
0.40 %

@time 3600 sec, pressure 40.0 mpa

0.40 %

@time 1.00 hour, pressure 5800 psi

180°c; iso 899
0.40 %

@pressure 20.0 mpa, time 3.60e+7 sec

0.40 %

@pressure 2900 psi, time 10000 hour

180°c; iso 899
0.40 %

@pressure 30.0 mpa, time 360000 sec

0.40 %

@pressure 4350 psi, time 100 hour

iso 899
0.50 %

@pressure 40.0 mpa, time 360000 sec

0.50 %

@pressure 5800 psi, time 100 hour

iso 899
0.50 %

@time 3600 sec, pressure 50.0 mpa

0.50 %

@time 1.00 hour, pressure 7250 psi

180°c; iso 899
0.55 %

@time 3600 sec, pressure 45.0 mpa

0.55 %

@time 1.00 hour, pressure 6530 psi

iso 899
0.60 %

@pressure 45.0 mpa, time 360000 sec

0.60 %

@pressure 6530 psi, time 100 hour

iso 899
0.78 %

@time 3600 sec, pressure 60.0 mpa

0.78 %

@time 1.00 hour, pressure 8700 psi

iso 899
0.80 %

@pressure 60.0 mpa, time 360000 sec

0.80 %

@pressure 8700 psi, time 100 hour

iso 899
0.80 %

@pressure 50.0 mpa, time 360000 sec

0.80 %

@pressure 7250 psi, time 100 hour

180°c; iso 899
0.90 %

@pressure 30.0 mpa, time 3.60e+7 sec

0.90 %

@pressure 4350 psi, time 10000 hour

iso 899
0.90 %

@pressure 60.0 mpa, time 3.60e+7 sec

0.90 %

@pressure 8700 psi, time 10000 hour

iso 899
0.99 %

@time 3600 sec, pressure 75.0 mpa

0.99 %

@time 1.00 hour, pressure 10900 psi

iso 899
1.1 %

@pressure 75.0 mpa, time 360000 sec

1.1 %

@pressure 10900 psi, time 100 hour

iso 899
1.23 %

@pressure 75.0 mpa, time 3.60e+7 sec

1.23 %

@pressure 10900 psi, time 10000 hour

iso 899
1.5 %

@pressure 40.0 mpa, time 3.60e+7 sec

1.5 %

@pressure 5800 psi, time 10000 hour

180°c; iso 899
2.5 %

@pressure 50.0 mpa, time 3.60e+7 sec

2.5 %

@pressure 7250 psi, time 10000 hour

180°c; iso 899
6.1 %

@pressure 45.0 mpa, time 3.60e+7 sec

6.1 %

@pressure 6530 psi, time 10000 hour

iso 899creep strength22.0 mpa

@time 3.60e+7 sec

3190 psi

@time 10000 hour

in water at 95°c
30.0 mpa

@time 3.60e+6 sec

4350 psi

@time 1000 hour

in water at 95°c
41.0 mpa

@time 360000 sec

5950 psi

@time 100 hour

in water at 95°c
55.0 mpa

@time 36000 sec

7980 psi

@time 10.0 hour

in water at 95°c弹性模量9.80 gpa

@temperature 160 °c

1420 ksi

@temperature 320 °f

iso 527
9.85 gpa

@temperature 60.0 °c

1430 ksi

@temperature 140 °f

iso 527
9.90 gpa

@temperature 20.0 °c

1440 ksi

@temperature 68.0 °f

iso 527
10.0 gpa

@temperature 120 °c

1450 ksi

@temperature 248 °f

iso 527拉伸模量10.0 gpa1450 ksiiso 527-2fatigue strength43.0 mpa

@# of cycles 1.00e+7

6240 psi

@# of cycles 1.00e+7

52.0 mpa

@# of cycles 1.00e+6

7540 psi

@# of cycles 1.00e+6

65.0 mpa

@# of cycles 100000

9430 psi

@# of cycles 100000

剪切模量0.200 gpa

@temperature 225 °c

29.0 ksi

@temperature 437 °f

iso 6721
0.900 gpa

@temperature 200 °c

131 ksi

@temperature 392 °f

iso 6721
0.950 gpa

@temperature 100 °c

138 ksi

@temperature 212 °f

iso 6721
1.00 gpa

@temperature 50.0 °c

145 ksi

@temperature 122 °f

iso 6721悬壁梁缺口冲击强度8.00 kj/m²3.81 ft-lb/in²iso 180/a
8.00 kj/m²

@temperature -30.0 °c

3.81 ft-lb/in²

@temperature -22.0 °f

iso 180/a悬壁梁无缺口冲击强度42.0 kj/m²

@temperature 120 °c

20.0 ft-lb/in²

@temperature 248 °f

iso 179/1eu
50.0 kj/m²

@temperature 25.0 °c

23.8 ft-lb/in²

@temperature 77.0 °f

iso 179/1eu
57.0 kj/m²

@temperature -25.0 °c

27.1 ft-lb/in²

@temperature -13.0 °f

iso 179/1eu
59.0 kj/m²

@temperature 0.000 °c

28.1 ft-lb/in²

@temperature 32.0 °f

iso 179/1eu