1010C2日本三菱PA6

1010c2日本三菱pa6--1010c2是一种聚酰胺6（尼龙6）材料,。该产品在亚太地区有供货,加工方式为:注射成型。

1010c2的主要特性有:阻燃/额定火焰/加工性能良好

1010c2注射：

干燥 单位制

干燥温度 80.0 °c

干燥时间 4.0 到 8.0 hr

料筒后部温度 230 到 235 °c

料筒中部温度 235 到 250 °c

料筒前部温度 240 到 260 °c

射嘴温度 240 到 270 °c

加工（熔体）温度 240 到 275 °c

模具温度 50.0 到 80.0 °c

注射速度 中等偏快

背压 3.00 到 10.0 mpa

螺杆压缩比 2.5:1.0

pa6 processing technology and precautions:

pa can be molded by injection molding, extrusion and blowmolding.

drying treatment: as pa6 is easy to absorb moisture, specialattention shall be paid to the drying before processing. if thematerial is packaged and supplied with waterproof material, thecontainer shall be kept closed. if the humidity is greater than0.2%, it is recommended to dry in hot air above 80 ℃ for 16 hours.if the material has been exposed to air for more than 8 hours,vacuum drying at 105 ℃ for more than 8 hours is recommended.

melting temperature: 230-280 ℃, 250-280 ℃ for reinforcedvarieties.

mold temperature: 80-90 ℃, mold temperature significantlyaffects the crystallinity, which in turn affects the mechanicalproperties of plastic parts. for structural parts, crystallinity isvery important, so it is recommended that the mold temperature is80-90 ℃. for thin-walled plastic parts with long process, it isalso recommended to apply higher die temperature. increasing themold temperature can improve the strength and stiffness of plasticparts, but reduce the toughness. if the wall thickness is greaterthan 3mm, it is recommended to use a low-temperature die at 20-40℃. for glass fiber reinforced materials, the mold temperature shallbe greater than 80 ℃.

injection pressure: generally between 750-1250bar (depending onmaterial and product design)

injection speed: high speed (slightly lower forreinforcement)

runner and gate: the setting time of pa6 is very short, so theposition of gate is very important. the gate aperture shall not beless than 0.5 * t (where t is the thickness of plastic parts). ifhot runner is used, the gate size should be smaller than that ofconventional runner, because hot runner can help prevent prematuresolidification of material. if a submerged gate is used, theminimum diameter of the gate shall be 0.75mm.