巴斯夫A3H巴斯夫A3H英文物性

physical propertiesmetricenglishcommentsmechanical propertiesmetricenglishcommentsthermal propertiesmetricenglishcommentsprocessing propertiesmetricenglishcomments

	basf ultramid® a3h un00002 nylon 66 (dry)
density	1.13 g/cc	0.0408 lb/in³	iso 1183
tensile strength, yield	82.0 mpa	11900 psi	iso 527
elongation at yield	7.5 %	7.5 %	iso 527
tensile modulus	2.97 gpa	431 ksi	iso 527
flexural modulus	2.74 gpa	397 ksi	iso 178
izod impact, notched (iso)	4.20 kj/m² @temperature -40.0 °c	2.00 ft-lb/in² @temperature -40.0 °f	iso 180
	5.30 kj/m² @temperature 23.0 °c	2.52 ft-lb/in² @temperature 73.4 °f	iso 180
charpy impact unnotched	nb @temperature -30.0 °c	nb @temperature -22.0 °f	iso 179
	nb @temperature 23.0 °c	nb @temperature 73.4 °f	iso 179
charpy impact, notched	0.250 j/cm² @temperature -40.0 °c	1.19 ft-lb/in² @temperature -40.0 °f	iso 179
	0.500 j/cm² @temperature 23.0 °c	2.38 ft-lb/in² @temperature 73.4 °f	iso 179
melting point	260 °c	500 °f	iso 3146
deflection temperature at 0.46 mpa (66 psi)	190 °c	374 °f	iso 75
deflection temperature at 1.8 mpa (264 psi)	73.0 °c	163 °f	iso 75
melt temperature	280 - 300 °c	536 - 572 °f
mold temperature	40.0 - 80.0 °c	104 - 176 °f
drying temperature	80.0 °c @time 7200 - 14400 sec	176 °f @time 2.00 - 4.00 hour
moisture content	<= 0.20 %	<= 0.20 %
injection pressure	3.45 - 10.3 mpa	500 - 1500 psi