300 f是一种热塑性聚烯烃，用于挤出或压延软膜。 300f还可用作挤出应用中聚丙烯均聚物的抗冲击/增韧改性剂。例如，在捆扎应用中，它显著降低了纤维颤动，并提高了薄膜在高拉伸比下的可加工性。 300 f可在任何传统pp挤出生产线上以及pvc日历上加工。也可在标准ldpe或lldpe薄膜生产线上进行吹塑。

有关法规遵从性信息，请参阅 300f法规事务产品管理信息/认证数据表（rapids）

300 f

聚烯烃

lyondellbasell industries

产品说明：

300 f is a thermoplastic polyolefin which has beendeveloped for the extrusion or calendering of soft film. 300 f can also be used as impact/toughener modifier ofpolypropylene homopolymer in extrusion applications. in strappingapplications for instance, it notably decreases fibrillation andimproves the processability of the film at high drawing ratios. 300 f can be processed on any conventional pp extrusionline as well as on pvc calendars. it can also be blown on standardldpe or lldpe film lines.
for regulatory compliance information see the adflex affairs product stewardship information/certificationdata sheet (rapids), which can be found on.

300 f 物性表

基本信息
特性

良好的柔韧性

食品接触的合规性

用途

薄膜

袋子

管件

瓶子

机构评级

fda 21 cfr 177.2600

形式

粒子

加工方法

薄膜挤出

吹塑成型

物理性能额定值单位制测试方法密度0.890g/cm³iso 1183/a熔流率（熔体流动速率） (230°c/2.16 kg)0.80g/10 miniso 1133硬度额定值单位制测试方法肖氏硬度 (邵氏d)36
iso 868机械性能额定值单位制测试方法拉伸模量
iso 527-2/25    0.0500 mm 1200mpaiso 527-2/25    0.0500 mm 2320mpaiso 527-2/25拉伸应力
    屈服9.00mpaiso 527-2    断裂, 0.0500 mm 318.0mpaiso 527-2/500    断裂, 50.0 mm 427.0mpaiso 527-2/500拉伸应变
    横向流量 : 屈服, 0.0500 mm28%iso 527-2/500    流量 : 屈服, 0.0500 mm20%iso 527-2/500    断裂500%iso 527-2弯曲模量330mpaiso 178tensile strength at yield 5
iso 527-3    md11.0mpaiso 527-3    td8.00mpaiso 527-3断裂伸长率 6
iso 527-3    md870%iso 527-3    td850%iso 527-3薄膜额定值单位制测试方法薄膜厚度 - 经测试50µm
冲击性能额定值单位制测试方法悬壁梁缺口冲击强度
iso 180/1a    -50°c40kj/m²iso 180/1a    -20°c70kj/m²iso 180/1a    23°c无断裂
iso 180/1a热性能额定值单位制测试方法热变形温度 (0.45 mpa, 未退火)50.0°ciso 75-2/b维卡软化温度75.0°ciso 306/a50光学性能额定值单位制测试方法光泽度 (45°, 50.0 µm)4
astm d2457雾度 (50.0µm)95%astm d1003