PC 1201-10韩国LG

pc 1201-10韩国lg---lupoy pc 1201-10 resin is designed forextrusion and injection molding products. it exhibits an excellentphysical property balance of heat resistance, transparency andimpact strength.

physical property  rating unit system test method

proportion one point two zero g/cm ³ astm d792

melt flow rate (mfr) (300 ° c/1.2 kg) ten g/10 min astmd1238

shrinkage flow 0.50 to 0.70 % astm d955

water absorption astm d570

twenty-three ° c, 24 hr zero point one five % astm d570

balance, 23 ° c, 50% rh zero point three two % astm d570

hardness rating unit system test method

rockwell hardness astm d785

grade m seventy-three astm d785

r class one hundred and eighteen astm d785

mechanical properties rating unit system test method

tensile modulus two thousand four hundred and ten mpa astmd638

tensile strength astm d638

yield, 23 ° c 1 sixty mpa astm d638

crack seventy-one mpa astm d638

elongation astm d638

yield six % astm d638

crack one hundred and fifty % astm d638

bending modulus two thousand four hundred and ten mpa astmd790

bending strength  ninety-six mpa astm d790

wear resistance - change in haze 2 forty-five % astm d1004

flammability rating unit system test method

average combustion degree three cm astm d635

impact property rating unit system test method

notched impact strength of cantilever beam 3 (23 ° c, 3.20 mm)nine hundred j/m astm d256

notchless cantilever impact (23 ° c) no fracture astm d256

dart impact 4 (23) with measuring instrument ° c, 3.20 mm, totalenergy) eighty-seven j astm d3763

thermal performance rating unit system test method

thermal deformation temperature under load astm d648

45 mpa, annealed, 4.00 mm one hundred and forty-four ° c astmd648

1.8 mpa, un annealed, 4.00 mm one hundred and twenty-eight ° castm d648

1.8 mpa, annealed, 4.00 mm one hundred and forty-one ° c astmd648

vicat softening temperature one hundred and forty-nine ° c astmd1525 5

ball pressure temperature >  one hundred and twenty-five° c iec 60598-1

linear coefficient of thermal expansion - flow (- 40 to 82) ° c)6.8e-5 cm/cm/ ° c astm d696

electrical performance rating unit system test method

volume resistivity (23 ° c) 2.0e+17 ohms·cm astm d257

dielectric strength seventeen kv/mm astm d149

dielectric constant (60 hz) three astm d150

dissipation factor (60 hz) 1.0e-3 astm d150

tracking index of leakage current (2.00 mm) two hundred andfifty v iec 60112

ul flame retardant rating ul 94

3.00 mm hb ul 94

0.500 mm v-2 ul 94

1.60 mm v-2 ul 94

2.50 mm v-2 ul 94

2.70 mm v-2 ul 94

hot filament ignition temperature 6 (2.00 mm) eight hundred andfifty ° c iec 60695-2-13

limiting oxygen index twenty-six % astm d2863