chemical abbreviation according to iso 1043-1: pom
molding compound iso 9988- pom-k, m-gnr, 04-002
pom copolymer
easy flowing injection molding type for precision molded partsand
thin-walled molded parts with high rigidity, hardness andtoughness;
good chemical resistance to solvents, fuel and strong alkalisas
well as good hydrolysis resistance; high resistance to thermaland
oxidative degradation.
monomers and additives are listed in eu-regulation (eu) 10/2011
fda compliant according to 21 cfr 177.2470
ul-registration for all colours and a thickness more than 1.5 mmas
ul 94 hb, temperature index ul 746 b electrical 110 °c,mechanical
90 °c.
burning rate iso 3795 and fmvss 302 < 75 mm/min for a thicknessmore than 1 mm.
ranges of applications: automotive engineering, precision
engineering, electric and electronical industry, domestic
appliances.
fda = food and drug administration (usa)
ul = underwriters laboratories (usa)
fmvss = federal motor vehicle safety standard (usa)
hostaform® c 13021 物性表
黄卡编号 | e42337-234597 |
特性 | 超高韧性 刚性,高 抗溶剂性 流动性中等 耐化学性良好 耐碱 耐燃油性 耐水解性 硬度高 |
机构评级 | fda 21 cfr 177.2470 欧洲 10/1/2011 12:00:00 am |
rohs 合规性 | 联系制造商 |
多点数据 | isothermal stress vs. strain (iso 11403-1) shear stress vs. shear rate (iso 11403-1) |
树脂id (iso 1043) | pom |
密度 | 1.41 | g/cm³ | iso 1183 |
溶化体积流率(mvr) (190°c/2.16 kg) | 12.0 | cm³/10min | iso 1133 |
收缩率 | iso 294-4 | ||
垂直流动方向 | 1.8 | % | iso 294-4 |
流动方向 | 2.0 | % | iso 294-4 |
吸水率 (饱和, 23°c) | 0.65 | % | iso 62 |
拉伸模量 | 2900 | mpa | iso 527-2/1a/1 |
拉伸应力 (屈服) | 65.0 | mpa | iso 527-2/1a/50 |
拉伸应变 (屈服) | 9.0 | % | iso 527-2/1a/50 |
标称拉伸断裂应变 | 25 | % | iso 527-2/1a/50 |
拉伸蠕变模量 | iso 899-1 | ||
1 hr | 2500 | mpa | iso 899-1 |
1000hr | 1300 | mpa | iso 899-1 |
弯曲模量 (23°c) | 2800 | mpa | iso 178 |
简支梁缺口冲击强度 | iso 179/1ea | ||
-30°c | 6.0 | kj/m² | iso 179/1ea |
23°c | 6.5 | kj/m² | iso 179/1ea |
简支梁无缺口冲击强度 | iso 179/1eu | ||
-30°c | 140 | kj/m² | iso 179/1eu |
23°c | 150 | kj/m² | iso 179/1eu |
热变形温度 (1.8 mpa, 未退火) | 106 | °c | iso 75-2/a |
熔融温度 1 | 166 | °c | iso 11357-3 |
线形热膨胀系数 - 流动 | 1.1e-4 | cm/cm/°c | iso 11359-2 |
表面电阻率 | 1.0e+14 | ohms | iec 60093 |
体积电阻率 | 1.0e+14 | ohms·cm | iec 60093 |
介电强度 | 35 | kv/mm | iec 60243-1 |
相对电容率 | iec 60250 | ||
100hz | 4.00 | iec 60250 | |
1 mhz | 4.00 | iec 60250 | |
耗散因数 | iec 60250 | ||
100hz | 2.0e-3 | iec 60250 | |
1 mhz | 5.0e-3 | iec 60250 | |
漏电起痕指数 | 600 | v | iec 60112 |
ul 阻燃等级 | ul 94 | ||
1.50mm | hb | ul 94 | |
3.00mm | hb | ul 94 |
density of melt | 1.200 | g/cm³ | 内部方法 |
ejection temperature | 165 | °c | 内部方法 |
specific heat capacity of melt | 2210 | j/kg/°c | 内部方法 |
thermal conductivity of melt | 0.16 | w/m/k | 内部方法 |
干燥温度 | 120 到 140 | °c | |
干燥时间 | 3.0 到 4.0 | hr | |
料斗温度 | 20.0 到 30.0 | °c | |
料筒后部温度 | 170 到 180 | °c | |
料筒中部温度 | 180 到 190 | °c | |
料筒前部温度 | 190 到 200 | °c | |
射嘴温度 | 190 到 210 | °c | |
加工(熔体)温度 | 190 到 210 | °c | |
模具温度 | 80.0 到 120 | °c | |
注塑压力 | 60.0 到 120 | mpa | |
注射速度 | 慢到中等 | ||
保压 | 60.0 到 120 | mpa | |
背压 | 0.00 到 4.00 | mpa |
manifold temperature: 190 to 210°czone 4 temperature: 190 to210°cfeed temperature: 60 to 80°c |
1 . | 10°c/min |