basf ultrason s 3010psu

polymer,thermoplastic,polysulfone(psu)basf产品说明:

ultrason s 3010 is an unreinforced, higher viscosity injectionmolding and extrusion psu grade, tougher and with improved chemicalresistance. it conforms to fda re of 21 cfr 177.1655.

 

basf ultrason s 3010 psu 物性表

物理性能额定值 (公制)额定值 (英制)测试方法

密度1.24g/cc0.0448lb/in³iso1183吸水率0.80%0.80%iso62平衡吸湿0.30%0.30%23°c/50%r.h.; iso 62粘度测试72cm³/g72cm³/gviscositynumber线性成型收缩率,flow0.0070cm/cm0.0070in/iniso294线性成型收缩率，横向0.0074cm/cm0.0074in/iniso294熔体流动速率40 g/10min

@load 10.0 kg, temperature 360 °c

40 g/10min

@load 22.0 lb, temperature 680 °f

iso1133

机械性能额定值 (公制)额定值 (英制)测试方法

球压硬度psiiso2039-1抗张强度(断裂)75.0mpa10900psi5mm/min;iso 527-2抗张强度20.0 mpa

@strain 1.00 %, temperature 160 °c

2900 psi

@strain 1.00 %, temperature 320 °f

iso527
27.0 mpa

@strain 1.00 %, temperature 23.0 °c

3920 psi

@strain 1.00 %, temperature 73.4 °f

iso527
35.0 mpa

@strain 2.00 %, temperature 160 °c

5080 psi

@strain 2.00 %, temperature 320 °f

iso527
47.0 mpa

@strain 2.00 %, temperature 23.0 °c

6820 psi

@strain 2.00 %, temperature 73.4 °f

iso527
70.0 mpa

@strain 4.00 %, temperature 23.0 °c

10200 psi

@strain 4.00 %, temperature 73.4 °f

iso527抗张强度(屈服)75.0mpa10900psi50mm/min;iso 527-2
40.0 mpa

@temperature 140 °c

5800 psi

@temperature 284 °f

58.0 mpa

@temperature 100 °c

8410 psi

@temperature 212 °f

68.0 mpa

@temperature 60.0 °c

9860 psi

@temperature 140 °f

75.0 mpa

@temperature 20.0 °c

10900 psi

@temperature 68.0 °f

伸长率(断裂)5.7%5.7%5mm/min;iso 527-2屈服伸长率5.7%5.7%50mm/min;iso 527-2
0.50 %

@time 3600 sec, pressure 10.0 mpa

0.50 %

@time 1.00 hour, pressure 1450 psi

iso899
0.55 %

@pressure 10.0 mpa, time 360000 sec

0.55 %

@pressure 1450 psi, time 100 hour

iso899
0.56 %

@pressure 10.0 mpa, time 3.60e+7 sec

0.56 %

@pressure 1450 psi, time 10000 hour

iso899
0.80 %

@time 3600 sec, pressure 20.0 mpa

0.80 %

@time 1.00 hour, pressure 2900 psi

iso899
0.90 %

@pressure 20.0 mpa, time 360000 sec

0.90 %

@pressure 2900 psi, time 100 hour

iso899
1.3 %

@time 3600 sec, pressure 30.0 mpa

1.3 %

@time 1.00 hour, pressure 4350 psi

iso899
1.4 %

@pressure 30.0 mpa, time 360000 sec

1.4 %

@pressure 4350 psi, time 100 hour

iso899
1.5 %

@pressure 30.0 mpa, time 3.60e+7 sec

1.5 %

@pressure 4350 psi, time 10000 hour

iso899
1.9 %

@time 3600 sec, pressure 40.0 mpa

1.9 %

@time 1.00 hour, pressure 5800 psi

iso899
2.0 %

@pressure 20.0 mpa, time 3.60e+7 sec

2.0 %

@pressure 2900 psi, time 10000 hour

iso899
2.0 %

@pressure 40.0 mpa, time 360000 sec

2.0 %

@pressure 5800 psi, time 100 hour

iso899
2.0 %

@time 3600 sec, pressure 42.0 mpa

2.0 %

@time 1.00 hour, pressure 6090 psi

iso899
2.2 %

@pressure 42.0 mpa, time 360000 sec

2.2 %

@pressure 6090 psi, time 100 hour

iso899
2.4 %

@pressure 40.0 mpa, time 3.60e+7 sec

2.4 %

@pressure 5800 psi, time 10000 hour

iso899
2.5 %

@pressure 42.0 mpa, time 3.60e+7 sec

2.5 %

@pressure 6090 psi, time 10000 hour

iso899creepstrength17.0 mpa

@time 3.60e+7 sec

2470 psi

@time 10000 hour

in waterat 95°c
20.0 mpa

@time 3.60e+6 sec

2900 psi

@time 1000 hour

in waterat 95°c
25.0 mpa

@time 360000 sec

3630 psi

@time 100 hour

in waterat 95°c
32.0 mpa

@time 36000 sec

4640 psi

@time 10.0 hour

in waterat 95°c弹性模量2.00 gpa

@temperature 140 °c

290 ksi

@temperature 284 °f

iso527
2.30 gpa

@temperature 100 °c

334 ksi

@temperature 212 °f

iso527
2.49 gpa

@temperature 60.0 °c

361 ksi

@temperature 140 °f

iso527
2.51 gpa

@temperature 20.0 °c

364 ksi

@temperature 68.0 °f

iso527拉伸模量2.60gpa377ksiiso527-2fatiguestrength25.0 mpa

@# of cycles 1.00e+7

3630 psi

@# of cycles 1.00e+7

30.0 mpa

@# of cycles 1.00e+6

4350 psi

@# of cycles 1.00e+6

40.0 mpa

@# of cycles 100000

5800 psi

@# of cycles 100000

50.0 mpa

@# of cycles 10000

7250 psi

@# of cycles 10000

剪切模量0.0250gpa

@temperature 200 °c

3.63 ksi

@temperature 392 °f

iso6721
0.800 gpa

@temperature 175 °c

116 ksi

@temperature 347 °f

iso6721
0.900 gpa

@temperature 100 °c

131 ksi

@temperature 212 °f

iso6721
0.950 gpa

@temperature 50.0 °c

138 ksi

@temperature 122 °f

iso6721悬壁梁缺口冲击强度5.50kj/m²2.62ft-lb/in²iso180/a
5.00kj/m²

@temperature 120 °c

2.38ft-lb/in²

@temperature 248 °f

iso179/1ea
6.00kj/m²

@temperature -30.0 °c

2.86ft-lb/in²

@temperature -22.0 °f

iso180/a
10.0kj/m²

@temperature 50.0 °c

4.76ft-lb/in²

@temperature 122 °f

iso179/1ea
13.0kj/m²

@temperature -25.0 °c

6.19ft-lb/in²

@temperature -13.0 °f

iso179/1ea简支梁无缺口冲击强度nbnbiso179/1eu
nb

@temperature -30.0 °c

nb

@temperature -22.0 °f

iso179/1eu简支梁缺口冲击强度0.550j/cm²2.62ft-lb/in²iso179/1ea
0.600j/cm²

@temperature -30.0 °c

iso179/1ea拉伸蠕变模量(1000 hr)2500mpa363000psiiso899-1

电气性能额定值 (公制)额定值 (英制)测试方法

体积电阻率>=1.00e+13 ohm-cm>=1.00e+13 ohm-cmiec60093表面电阻>=1.00e+14 ohm>=1.00e+14 ohmiec60093介电常数3.1

@frequency 100 hz

3.1

@frequency 100 hz

iec60250
3.1

@frequency 1.00e+6 hz

3.1

@frequency 1.00e+6 hz

iec60250介电强度37.0kv/mm940kv/iniec60243-1耗散因数0.00080

@frequency 100 hz

0.00080

@frequency 100 hz

iec60250
0.0064

@frequency 1.00e+6 hz

0.0064

@frequency 1.00e+6 hz

iec60250相比耐漏电起痕指数(cti)uid a & b; iec 60112

热性能额定值 (公制)额定值 (英制)测试方法

线形热膨胀系数 -流动53.0µm/m-°c

@temperature 23.0 - 80.0 °c

29.4µin/in-°f

@temperature 73.4 - 176 °f

iso11359-1/-2
60.0µm/m-°c

@temperature 140 - 180 °c

33.3µin/in-°f

@temperature 284 - 356 °f

iso11359-1/-2