CYCOLOY C3650 沙伯基础 阻燃PC/ABS

mechanical机械性能

tensile stress, yld, type i, 50mm/min / 抗拉强度,屈服,类型i,50 mm/min

57

mpa

astm d 638

tensile strain, yld, type i, 50mm/min / 拉伸伸长, 屈服, 类型i, 50 mm/min

5

%

tensile strain, brk, type i, 50mm/min / 拉伸伸长,断裂,类型i, 50 mm/min

150

tensile modulus, 50 mm/min /拉伸模量,50 mm/min

2270

flexural stress, yld, 1.3 mm/min,50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距

88

astm d 790

flexural modulus, 1.3 mm/min, 50mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距

2340

impact

izod impact, notched, 23°c /悬臂梁缺口冲击强度23°c

587

j/m

astm d 256

izod impact, notched, -30°c /悬壁梁缺口冲击强度, -30°c

480

instrumented impact total energy,23°c / 仪表控制抗冲击总能量，23°c

54

j

astm d 3763

instrumented impact total energy,-30°c / 装有测量仪表的落镖冲击total energy，-30°c

thermal

hdt, 0.45 mpa, 3.2 mm, unannealed/ 热变形温度,0.45 mpa, 3.2 mm,未退火

129

°c

astm d 648

hdt, 1.82 mpa, 3.2mm, unannealed/ 热变形温度,1.82 mpa, 3.2mm,未退火

112

cte, -40°c to 40°c, flow /线形膨胀系数,-40°c 到40°c,流动

7.2e-05

1/°c

astm e 831

vicat softening temp, rate b/50 /维卡软化温度 b级/50

130

iso 306

relative temp index, elec /相对热指数， 电性能

105

ul 746b

relative temp index, mechw/impact / 相对热指数，机械冲击性能

80

relative temp index, mech w/oimpact / 相对热指数，非机械冲击性能

physical

specific gravity/比重

1.15

–

astm d 792

mold shrinkage, flow, 3.2 mm /模塑收缩量，流动，3.2 mm

0.5 – 0.7

sabic method

melt flow rate / 熔流率, 260°c/5.0kgf

19

g/10 min

astm d 1238

electrical

hot wire ignition {plc) / 热丝引燃{plc)

3

plc code

ul 746a

high ampere arc ign, surface{plc} / 高电流电弧引燃，表面{plc}

1

comparative tracking index (ul){plc} / 漏电起痕指数 (ul) {plc}

2

flame characteristics火焰特性

ul recognized, 94hb flame classrating (3) / ul认可，94hb 阻燃等级(3)

1.19

mm

ul 94

csa (see file for completelisting)

ls88480

file no.

csa listed