日本油墨30%玻纤高抗冲PPS Z-230

molding shrinkage

flow

0.30

%

across flow

1.2

water absorption (24 hr, 23°c)

0.020

nominal value

unit

test method

rockwell hardness (r-scale)

118

tensile modulus

9300

mpa

tensile strength

155

tensile elongation (break)

2.4

flexural modulus

8500

flexural strength

220

flexural elongation (break)

3.2

compressive strength

150

poisson&＃39;s ratio

0.36

nominal value

notched izod impact

140

j/m

unnotched izod impact

750

deflection temperature under load (1.8 mpa, unannealed)

255

°c

clte

flow : -30 to 100°c

2.2e-5

cm/cm/°c

transverse : -30 to 100°c

volume resistivity

1.0e+16

ohms·cm

dielectric strength (1.60 mm)

16

kv/mm

dielectric constant (1 mhz)

5.00

dissipation factor (1 mhz)

5.0e-3

nominal value

flame rating (1.6 mm)

v-0