pa46 ts300荷兰---supply pa46 / ts250f6 characteristic remarks: 30%glass reinforced, heat stable, flame retardant
main properties: 30% glass fiber, heat stabilizer, heatstability, flame retardant. important parameters: density: 1.68 g /cm3 molding shrinkage: 0.4% notch impact strength: 11 tensilestrength: 180 mpa bending modulus: 12000 mpa
main properties: 40% glass fiber, heat stabilizer, heatstability, flame retardant. important parameters: density: 1.77 g /cm3 molding shrinkage: 0.6% notch impact strength: 12 tensilestrength: 195 mpa bending modulus: 13000 mpa
main properties: 30% glass fiber, flame retardant, flameretardant. important parameters: density: 1.56 g / cm3 moldingshrinkage: 1.0% notched impact strength: 8 tensile strength: 170mpa bending modulus: 10000 mpa
main properties: 40% glass fiber, flame retardant, flameretardant. important parameters: density: 1.65 g / cm3 moldingshrinkage: 1.3% notched impact strength: 8 tensile strength: 180mpa bending modulus: 14000 mpa
supply pa46 / ts300 nc important parameters: density: 1.41 g /cm3 water absorption: 2.6% molding shrinkage: 1.3% bending modulus:3900 mpa hot deformation temperature: 290 ℃
supply pa46 / ts350 bk main performance: flame retardant, flameretardant. important parameters: density: 1.41 g / cm3 waterabsorption: 2.6% molding shrinkage: 1.3% bending modulus: 3900 mpahot deformation temperature: 290 ℃
main properties: 30% glass fiber, heat stabilizer, heatstability. important parameters: density: 1.41 g / cm3 waterabsorption: 1.5% notched impact strength: 12 tensile strength: 210mpa elongation at break: 4%
pa46 / tw200fm33 bk main properties: 30% glass / mineral, lowwarpage. important parameters: density: 1.42 g / cm3, notchedimpact strength: 16, tensile strength: 250 mpa, bending modulus:14000 mpa, hot deformation temperature: 290 ℃
supply pa46 / tw241f6 characteristics remarks: 30% glass fiberreinforced, heat stabilizer, lubricant, heat stable, lubrication.important parameters: density: 1.41 g / cm3 molding shrinkage: 1.2%notch impact strength: 4 bending modulus: 4700 mpa hot deformationtemperature: 290 ℃
pa46 / tw241f8 bk main properties: 40% glass fiber, heatstabilizer, lubricant, lubrication, thermal stability. importantparameters: density: 1.51 g / cm3 molding shrinkage: 1.1% notchimpact strength: 14 bending modulus: 11500 mpa hot deformationtemperature: 290 ℃
main properties: 50% glass fiber, heat stabilizer, heatstability. important parameters: density: 1.62 g / cm3, notchedimpact strength: 16, tensile strength: 250 mpa, tensile modulus:7800 mpa, hot deformation temperature: 290 ℃
supply pa46 / tw241f12 main performance: 60% glass fiber, heatstabilizer, good fluidity, thermal stability. important parameters:density: 1.27 g / cm3, water absorption: 2.9%, molding shrinkage:1.5%, bending modulus: 3100 mpa, hot deformation temperature: 200℃
main properties: 50% glass fiber, heat stabilizer, heatstability. important parameters: density: 1.63 g / cm3, waterabsorption: 1.8%, molding shrinkage: 1.3%, bending modulus: 11000mpa, hot deformation temperature: 285 ℃
main properties: 30% glass fiber, heat stabilizer, heatstability. important parameters: density: 1.54 g / cm3 moldingshrinkage: 0.5% tensile strength: 190 mpa elongation at break: 3%hot deformation temperature: 290 ℃
main properties: heat stabilizer, heat stability. importantparameters: density: 1.18 g / cm3, molding shrinkage: 2.0%, hotdeformation temperature: 190 ℃
the company's adequate supply, variety, reasonable price. inaddition, other raw material brands cannot be introduced in detail,and specific matters (physical property, , ul report, roshstandard, sgs test report, etc.)